14NiCrMo13-4 Alloy Steel DIN 1.6657
14NiCrMo13-4 Alloy Steel as also named in US standards is a case hardening steel
used in forgings to eg rock drilling tools. It can be used to make gear parts
exposed to the highest stresses and wear conditions. Typical components include
gears, planet wheels, drive pinions, shafts, bushes, and sleeves. Results in
high core strength and excellent toughness in the components and are very
suitable for parts with a large diameter.
EN36C can be used to make gear parts exposed to highest stresses and wear
conditions. Typical components include gears, planet wheels, drive pinions,
shafts, bushes and sleeves. Results in high core strength and excellent
toughness in the components and is very suitable for parts with large diameter.
2.All Grades Comparison
DIN EN ANFOR BS
1.6657 14NiCrMo13-4 16NCD13 832M13 / EN36C
3.Quality Standard
EN 10084 Case hardening steels
DIN17210 Case hardening steels
AS1444 Wrought alloy steels
4.Chemical Composition(%)
EN36B0.12-0.180.30-0.600.35 max0.025 max0.025
max0.60-1.103.00-3.75EN36C0.12-0.180.30-0.600.35 max0.025 max0.025
max0.60-1.103.00-3.750.10-0.25
Steel Grade C Mn Si P S Cr Ni Mo
14NiCrMo13-4 0.11-0.17 0.30-0.60 0.40 max 0.025 max 0.025 max 0.80-1.10
3.00-3.50 0.20-0.30
EN36A 0.10-0.16 0.35-0.60 0.35 max 0.025 max 0.025 max 0.70-1.00 3.00-3.75 /
6.HEAT TREATMENT:
Soft Annealing: Heat EN36C to 825oC, cool slowly. This will produce a maximum
Brinell hardness of 217.
Hardening: Harden from a temperature of 825-850oC, followed by oil or quenching.
Tempering:¨C After carburising and hardening, the steel is tempered between 140¡ãC
and 200¡ãC as required.
For use in the non carburised heat treated condition, temper in accordance with
properties required.
7.Welding:
Pre-heat welding area to 250-450¡ãC and maintain this temperature while welding
with a low hydrogen electrode. Cool at a maximum rate of 100¡ãC per hour. Do not
weld after carburising.
14NiCrMo13-4 Alloy Steel
All Grades Comparison
DIN EN ANFOR BS
1.6657 14NiCrMo13-4 16NCD13 832M13 / EN36C
14NiCrMo13-4 Alloy Steel Chemical Composition(%)
Steel Grade C Mn Si P S Cr Ni Mo
14NiCrMo13-4 0.11-0.17 0.30-0.60 0.40 max 0.025 max 0.025 max 0.80-1.10
3.00-3.50 0.20-0.30
Shape and size range
1.Shape: round, flat, square.
2.Size Range:
Round : Diameter(mm):1.0-1000, Length(mm):2000-11800.
Square: Diameter(mm):10-1000, Length(mm):2000-11800.
Flat: Thickness(mm):4-800, Width(mm):80-20000(mm), Length:2000-11800.
Mechanical Properties
Process Tensile Strength Rm (Mpa) Elongation A5 (%) Impact Value Kv (J) Room
Temperature Hardness (HB)
SOFT ANNEALED / / / / 217 max
QUENCHED AND TEMPERED 1230-1480 9 min 35 min / 368-424
Heat Treatment
Soft Annealing: Heat EN36C to 825oC, cool slowly. This will produce a maximum
Brinell hardness of 217.
Hardening: Harden from a temperature of 825-850oC, followed by oil or quenching.
Tempering:¨C After carburizing and hardening, the steel is tempered between 140¡ãC
and 200¡ãC as required.
For use in the non carburized heat treated condition, temper in accordance with
properties required.
Application:
Alloyed case hardening steel for parts with a required core tensile strength of
1000 ¨C 1300 N/mm² and good wearing resistance as boxes, piston bolts, spindles,
camshafts, gears, shafts and other mechanical controlling parts.Especially in
wheels and stopcock.
AISI 8620 1,6523 | 21NiCrMo2 | SNCM220 20NiCrMo13-4 1.6660 ASTM 52100 | 1,3505 | 100Cr6 | SUJ2 | EN31 33NiCrMoV14-5 1.6956
AISI 4340 | 36CrNiMo4 | 1,6511 | EN24 | 817M40 | SNCM439 EN DIN 34CrNiMo6 | 1,6582 | 4337 Engineering Steel BS EN 42CrMo4 | 1,7225 Alloy Steel
1,2379 | X153CrMo12 | SKD11 UNS S31254 1.4547 F44 Super Austenitic Stainless Steel DIN 1.6657 14NiCrMo13-4 16NCD13 832M13 EN36C
DIN1.6587 X4317 18CrNiMo7-6 17CrNiMo6 18NCD DIN 1.6566 17NiCrMo6-4 18NiCrMo5 817M17 SAE4317 DIN 1.6657 14NiCrMo13-4 16NCD13 832M13 EN36C